Abstract
Gold (Au) nanoparticles were prepared by sputter deposition of Au metal in an ionic liquid (IL) of 1-butyl-3-methylimidazolium hexafluorophosphate (BMI-PF6). The size of Au nanoparticles was increased from 2.6 to 4.8 nm by heat treatment at 373 K. The nanoparticles uniformly dispersed in the IL were densely immobilized on a glass substrate surface modified with a silane coupling agent having an imidazole functional group by spreading the Au particle IL solution on the substrates, followed by heat treatment at 373 K. The optical property of the thus-obtained films was tunable by controlling the size of Au nanoparticles in the IL and the degree of immobilization. An intense localized surface plasmon resonance (LSPR) peak was observed in each Au particle film, and the wavelength of the LSPR peak could be controlled by changing the size of nanoparticles in the IL solution before immobilization. Photoexcitation of the LSPR peak caused enhancement of the photoluminescence of CdTe nanoparticles immobilized on Au nanoparticle films, probably due to the locally enhanced electric field formed around Au nanoparticles.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.