Abstract
The fatigue life of cross-ply composite laminates was evaluated using a statistical model. A modified shear-lag analysis was applied to describe the cycle-number-dependent stiffness reduction and consequent stress redistribution processes in the laminates resulted from both progressive transverse matrix cracking in transverse plies and local delamination at tips of transverse cracks. From the strength degradation behaviour and the static strength distribution of 0° plies as well as the fatigue behaviour of 90° plies, the fatigue life of cross-ply laminates with various types of lay-up can be simulated from the model. Predictions of fatigue performance are compared with experimental data for [0/902]s, [02/902]s and [02/904]s graphite/epoxy cross-ply laminates: good agreements are obtained.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.