Abstract
The shrinkage variation of Low Temperature Cofired Ceramics(LTCC) limits the size of the substrates that impose limitations on embedded passive components. This paper focuses on the method of minimizing or controlling planar shrinkage and reducing distortion during firing. The laminated sheets of alumina and glass were sintered at varying temperature, and depending on the amount of the glass ceramics. When the sintered of multi-layer structure with Al2O3/Glass/Al2O3, the glass infiltrated entirely into Al2O3 layer at the temperature of about 950°C or higher.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.