Abstract
Grain growth and grain boundary character distribution relationships in Fe-Ga rolled sheet is investigated to study the influence of H2S gas content in argon on the development of selective grain growth through secondary recrystallization. Abnormal growth of (011) grains was predominant at the low content of H2S gas, while (113) grain growth was well developed at contents higher than 1.33% H2S. On the other hand, the development of (001) grains was challenging to produce because it is very sensitive to the anneal environment and has a relatively low fraction of high energy grain boundaries associated with misorientation angles that determine the mobility of boundaries.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.