Abstract
Coatings on low activation steels are required in fusion technology in order to reduce the tritium permeation rate through the steel into the cooling water system by a factor of at least 100. Alumina seems to be a promising coating material. However, an appropriate coating system must also have the potential for self-healing since the ceramic alumina scale tends to fail if mechanical stress is applied. A technology is introduced here to form a ductile Al enriched surface scale on Manet II steel (Fe-10.3%Cr) with an alumina overlayer. This technology consists of two main process steps. Hot dip aluminising has been performed at 700°C for 30 s in order to introduce Al to the near surface zone. The very hard intermetallic scale Fe 2Al 5 which forms during the immersion process gets completely transformed into FeAl 2, FeAl and α-Fe(Al) phases during a subsequent hot isostatic press (HIP) process step at high pressure at 1040°C for 30 min. The pressures chosen for the HIPing were 1000 and 2000 bar. Without HIPing pores form due to the Kirkendall effect. The influence of the high pressure on the heat treatment (1040°C, 30 min) will be discussed in this paper.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.