Role of Re in NiAl bond coating on intermittent isothermal oxidation behavior of thermal barrier coatings (TBCs) was researched in this study. Isothermal oxidation behaviors of NiAl-YSZ coatings with and without Re were investigated at 1100 ℃. Results showed that NiAlRe-YSZ coating revealed lower level of β to γ′ phase transformation, and less severe delamination of YSZ was observed compared with NiAl-YSZ coating after 300 h oxidation. Moreover, the synergistic effect of Re and Zr/Y jointly improved delamination resistance of NiAlRe-YSZ coating during oxidation. Severe internal oxidation and rumpling prompted the delamination of YSZ for NiAl-YSZ coating without Re.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.