Abstract
Large lattice mismatched heterostructures In0.78Ga0.22As/GaAs were grown with a low-temperature (LT) InGaAs buffer. Misfit dislocation arrays were observed at the LT-buffer/GaAs interfaces. Transmission electron microscopy (TEM) was used to investigate the microstructures of the heterointerfaces. The relationship between misfit dislocations and strain relaxation at the interface was analysed. It was found that strain redistribution gives rise to the discrepancy of interfacial structure and misfit strain relaxation for different samples. The experimental results are in favor of the conclusion and confirm the analysis we proposed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.