Reforming of bioethanol over Ni/Al 2O 3 and Ni/CeZrO 2/Al 2O 3 catalysts in supercritical water for hydrogen production

Abstract

Bioethanol was reformed in supercritical water (SCW) at 500 °C and 25 MPa on Ni/Al 2O 3 and Ni/CeZrO 2/Al 2O 3 catalysts to produce high-pressure hydrogen. The results were compared with non-catalytic reactions. Under supercritical water and in a non-catalytic environment, ethanol was reformed to H 2, CO 2 and CH 4 with small amounts of CO and C2 gas and liquid products. The presence of either Ni/Al 2O 3 or Ni/CeZrO 2/Al 2O 3 promoted reactions of ethanol reforming, dehydrogenation and decomposition. Acetaldehyde produced from the decomposition of ethanol was completely decomposed into CH 4 and CO, which underwent a further water–gas shift reaction in SCW. This led to great increases in ethanol conversion and H 2 yield on the catalysts of more than 3–4 times than that of the non-catalytic condition. For the catalytic operation, adding small amounts of oxygen at oxygen to ethanol molar ratio of 0.06 into the feed improved ethanol conversion, at the expense of some H 2 oxidized to water, resulting in a slightly lower H 2 yield. The ceria–zirconia promoted catalyst was more active than the unpromoted catalyst. On the promoted catalyst, complete ethanol conversion was achieved and no coke formation was found. The ceria–zirconia promoter has important roles in improving the decomposition of acetaldehyde, the enhancement of the water–gas shift as well as the methanation reactions to give an extremely low CO yield and a tremendously high H 2/CO ratio. The SCW environment for ethanol reforming caused the transformation of gamma–alumina towards the corundum phase of the alumina support in the Ni/Al 2O 3 catalyst, but this transformation was slowed down by the presence of the ceria–zirconia promoter.