Cemented carbides processed from WC-Ni-Co-Cr3C2-TiAl3 powder mixtures by HIP after sintering present a homogeneous precipitation of gamma prime in their metallic binder phases. Other reaction products include alumina precipitates and (Tix,W 1-x)C mixed carbides. The formation of these phases is consistent with the highly exothermic reactions detected by DSC during the heating ramp of the sintering cycle. The amount of alumina and gamma prime phases present in the sintered materials depends on the oxygen content of the powder mixtures. Refinement of gamma prime precipitates depends critically on the cooling rate after HIPing. Nanoindentation experiments have confirmed the presence of age hardening effects of samples which were previously solution treated. As expected, gamma prime precipitation is induced at lower temperatures in compositions with higher Al contents in the binder phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Refractory Metals and Hard Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.