Abstract
In this paper, the metal to ceramic transition of the Al–N 2 system was investigated using classical reactive pulsed-DC magnetron sputtering and HIgh Power Impulse Magnetron Sputtering (HIPIMS) at a constant average current of 3 A. Optical emission spectroscopy measurements revealed more ionised aluminium species in the HIPIMS discharge compared to pulsed-DC sputtering. It also showed excited N 0 and ionised N + species in reactive Ar/N 2 HIPIMS discharges. The corresponding evolution of the consumed nitrogen flow as a function of the N 2 partial pressure revealed that a higher amount of reactive gas is needed to achieve stoichiometric AlN with HIPIMS. Electron probe micro-analysis and X-ray diffraction measurements confirmed that a partially poisoned aluminium target is enough to allow the deposition of stoichiometric hcp-AlN thin films via HIPIMS. To go further in the comparison of both processes, two stoichiometric hexagonal aluminium nitride thin films have been deposited. High power impulse magnetron sputtered hcp-AlN exhibits a higher nano-hardness (18 GPa) than that of the coating realised with conventional pulsed-DC sputtering (8 GPa).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.