Abstract
Single crystals of Langasite La3Ga5SiO14 (LGS) were irradiated by 1 MeV Kr2+ ions at temperature range from 298 to 898 K in order to simulate the damage effect of neutron radiation on Langasite, a candidate sensor material proposed as high temperature and pressure sensors in nuclear reactors. The microstructure evolution of LGS as functions of irradiation dose and temperature was followed by in-situ TEM observation through electron diffraction pattern. LGS is found to be sensitive to ion beam irradiation-induced amorphization from displacive heavy ions with a low critical dose of ∼0.5 ± 0.2 dpa (neutron fluence of (1.6 ± 0.6 ) × 1019 neutrons/cm2) at room temperature. The critical amorphization temperature, Tc, is determined to be 910 ± 10 K. Under simultaneous ionizing electron (300 keV, 45 nA) and displacive heavy ion irradiations (1-MeV Kr2+ and flux of 6.25 × 1011 ions/cm2·s), LGS displayed greater stability of crystal structure against amorphization, possibly due to the electron radiation-induced recovery of displacive damage by heavy ions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.