Abstract
We report on a quantum dots-in-a-well infrared photodetector (DWELL QDIP) grown by metal organic vapor phase epitaxy. The DWELL QDIP consisted of ten stacked InAs/In0.15Ga0.85As/GaAs QD layers embedded between n-doped contact layers. The density of the QDs was about 9 x 1010 cm-2 per QD layer. The energy level structure of the DWELL was revealed by optical measurements of interband transitions, and from a comparison with this energy level scheme the origin of the photocurrent peaks could be identified. The main intersubband transition contributing to the photocurrent was associated with the quantum dot ground state to the quantum well excited state transition. The performance of the DWELL QDIPs was evaluated regarding responsivity and dark current for temperatures between 15 K and 77 K. The photocurrent spectrum was dominated by a LWIR peak, with a peak wavelength at 8.4 μm and a full width at half maximum (FWHM) of 1.1 μm. At an operating temperature of 65 K, the peak responsivity was 30 mA/W at an applied bias of 4 V and the dark current was 1.2×10-5 A/cm2. Wavelength tuning from 8.4 μm to 9.5 μm was demonstrated, by reversing the bias of the detector.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.