Abstract
In this work, the pulse electrodeposition technique has been employed for the first time to deposit SnSe films from a bath containing Analar grade 50 mM tin chloride (SnCl4) and 5 mM SeO2. The XRD profile of SnSe thin films deposited at different duty cycles indicate the peaks corresponding to SnSe. Atomic force microscopy studies indicated that the surface roughness increased from 0.5 to 1.5 nm with duty cycle. The transmission spectra exhibited interference fringes. The value of refractive index at 780 nm was 2.1, this value decreased to 1.95 with decrease of duty cycle. The room temperature resistivity increased from 0.1 to 10 Ωcm with decrease of duty cycle. Photo electrochemical cell studies were made using the films deposited at different duty cycles. For duty cycles greater than 15% photo output was observed. For a film deposited at 50% duty cycle, an open circuit voltage of 0.55 V and a short circuit current density of 5.0 mA cm−2 at 60 mW cm−2 illumination. Capacitance voltage measurements indicated Vfb = 0.67 V (SCE) and p type, carrier density = 6.98 × 1016 cm−3.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.