Abstract
AbstractThe growth of erbium doped GaAs by molecular beam epitaxy (MBE) can, depending on growth conditions, result in the precipitation of small spherical particles of erbium arsenide. It has been observed that by reducing the V:III (As:Ga) flux ratio to close to stoichiometry wirelike precipitates roughly aligned in the direction of growth are produced. The concentration of erbium incorporated into the GaAs lattice for a constant erbium flux is also affected by the As:Ga flux ratio with an increase in erbium doping being observed with decreasing As:Ga flux ratio.Electrical measurements have been performed on erbium doped GaAs samples co-doped with selenium, an n-type dopant. Measurements have revealed that when erbium is present, the electron concentration is reduced by an amount approximately equal to 70% of the erbium concentration. DLTS measurements have shown that although large concentrations of deep levels are present in erbium doped material, the measured concentration of these deep levels is not high enough to account for the observed reduction in electron concentration with erbium doping.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.