Abstract
The ZrB2 powders with different morphology were prepared by pressureless reactions, using ZrO2, B2O3, B4C, and graphite as raw materials. Three kinds of chemical reaction system were employed. The ratio of raw materials and reaction temperature were adjusted to prepare ZrB2 powders of different morphology and particle size. The phase composition and purity of the as-prepared powders were analyzed by XRD, while the morphology and particle size were analyzed by SEM. The ZrB2 powders were purified by removing impurities at 600 °C in a muffle furnace in air atmosphere. The results showed that in the reaction systems of ZrO2-B2O3-C and ZrO2-B4C-C, the ZrB2 could be generated at 1500 °C. The morphology of the as-prepared ZrB2 powders were particles, rod-like or near spherical for ZrO2-B2O3-C system and particles for ZrO2-B4C-C system. In the reaction system of ZrO2, B2O3, B4C, and C with a mole ratio of 3:2:1:8, the ZrB2 powders with high purity could be produced at 1700 °C. The ZrB2 powder was near spherical. After heat treatment, the particle size and morphology changed to some extent.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.