Abstract
Magnetic polymer composite microspheres with high magnetite contents were prepared by dispersion polymerization of styrene (St) and glucidylmethacrylate (GMA), in which Fe 3O 4 nanoparticles were co-stabilized by oleic acid and silane surfactants. The microstructure of the composite microspheres was characterized by Fourier transform infrared (FTIR) spectrometry, X-ray diffraction (XRD) and transmission electron microscopy (TEM). Results demonstrated the presence of a hybrid morphology with organic polymer-encapsulated inorganic particles. Subsequently, thermogravimetric analysis (TGA) and vibrating sample magnetometry (VSM) were used to evaluate the magnetite content of the microspheres. It was found that an accordant magnetite content of about 70 wt%, could be obtained for the magnetic polymer microspheres, a value significantly higher than those reported thus far. The possible mechanism for the formation of the microspheres was proposed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.