Abstract
The electric-current sintering technique was used to fully densify hydrogenation–disproportionation–desorption–recombination (HDDR)-processed Nd–Fe–B powder at temperatures below the grain growth temperature in order to produce high-coercive bulk magnets. However, the sintered magnets exhibited anomalous coercivity reduction that depended on sintered density. Reheating examination of the sintered magnets revealed that the reduced coercivity was increased in proportion to the heating temperature, resulting in complete recovery of coercivity. As a result, the combination of electric-current sintering and post-annealing produced sintered magnets with a coercivity of 15kOe. Scanning and transmission electron microscopy revealed no evidence that associated the anomalous coercivity reduction and recovery with grain boundary morphology. On the other hand, various HDDR powders with different particle sizes were sintered, and finer powders yielded lower coercivity after sintering, implying that the anomalous coercivity reduction was associated with particle surface oxides of the raw powder.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.