Abstract
Mg−Si binary oxides were prepared by the sol-gel method, using magnesium diethoxide and tetraethoxysilane as starting materials. Mg−Si mixed oxides were prepared at pH3 and 9 at nominal concentrations of 1.3, 4.0, and 6.7 mole% MgO. Density and strength of the acid sites were determined by pyridine thermal programmed desorption. Comparable Lewis acidity was found in pH3 and 9 preparations. However, when the samples were sulfated with sulfuric acid, strong Bronsted acidity was developed, reaching a maximum at 6.7 mole% MgO. The strong acidity of sulfated samples was corroborated using the isopropanol decomposition reaction as catalytic test. Similar conversions are obtained at 100°C on sulfated samples, whereas 260°C are required for non-sulfated ones.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.