Abstract
ABSTRACTA modified resin was synthesized through the reaction between dodecylamine and tetraglycidyldiaminodiphenylmethane (TGDDM), which was used as the film former of sizing agent for carbon fiber (CF). The sizing agents were prepared through phase inversion emulsification method. Fourier transform infrared spectroscopy (FTIR) was utilized to analyze the modified resin. Particle sizes of the sizing agents were tested to evaluate their stabilities. Differential scanning calorimetry (DSC) results demonstrated that the glass transition temperature (Tg) of the modified TGDDM is much higher than the Tg of the cured epoxy resin E‐44. The influences of the sizing treatment on CF were investigated by abrasion resistance, fluffs, and stiffness tests. The maximum abrasion resistance increased by 172.8%, compared with the abrasion resistance of the desized CF. Interlaminar shear strength (ILSS) results of the CF/TGDDM composites indicated that the interfacial adhesion between CF and matrix resin was greatly improved after CF was sized. The maximum ILSS value could obtain a 29.16% improvement, compared with the ILSS of the desized CF composite. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015, 132, 41882.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.