Abstract

A crack-free asymmetric membrane of perovskite-type oxide (La 0.6Sr 0.4Co 0.2Fe 0.8O 3− δ ) was successfully prepared by coating a slurry containing La 0.6Sr 0.4Co 0.2Fe 0.8O 3− δ powders directly on the surface of a green support of the same composition, followed by sintering. It was found that crack-free asymmetric membranes could be obtained by controlling the powder concentration of the slurry in the range of 15–25 wt.%. After sintering, the crystal phase of the top layer of asymmetric membranes prepared was the same as that of powders, which were of the cubic perovskite phase. The nitrogen permeability and SEM photograph of the support showed that the support was porous, and the gas-tight test and SEM demonstrated that the top layer of asymmetric membrane was dense and crack-free. The asymmetric membrane prepared, whose dense top layer was 200 μm thick, exhibited about three to four times as high an oxygen flux as a 2 mm dense sintered disc.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.