Abstract
The solid wastes fly ash and aluminum dross were used to prepare the low cost, high added-value product spinel-corundum-Sialon with anin situaluminothermic reduction-nitridation reaction. The effects of varying raw material components and heating temperatures on the phase compositions, microstructure, bulk density, apparent porosity, and bending strength of products were investigated. The presence of hazardous or impure elements in the products was also evaluated. The sintered materials mainly consisted of micro-/nanosized plate corundum, octahedral spinel, and hexagonal columnarβ-Sialon. The bulk density and bending strength of product samples initially increased and then decreased as Al content increased. Product samples with an Al content exceeding 10 mass% that were sintered at 1450°C exhibited the highest bending strength (288 MPa), the lowest apparent porosity (1.24%), and extremely low linear shrinkage (0.67%). The main impurity present was Fe5Si3with hazardous elements P, Cr, Mn, and Ni doping. This work could provide a new method to reduce environmental pollution and manufacture low cost high performance refractory materials using the abundant waste materials fly ash and aluminum dross.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.