Metal-matrix nanocomposite, composed of copper/20wt.% Al2O3, was fabricated by mechanical alloying method. The starting powders mixture was milled in planetary ball mill up to 20h. The effect of milling time on the properties of the obtained powders was studied. X-ray diffraction analysis (XRD) and transmission electron microscopy (TEM) were used to investigate phase composition, crystal size and morphology of the milled powders. To study the sinterability, the milled nanocomposite powders were cold pressed and sintered in argon atmosphere at different firing temperatures, i.e. 700°, 800° and 850°C, for 1h. Physical properties, namely, bulk density and apparent porosity of sintered bodies were determined by Archimedes method. Phase identification and microstructure of the sintered composites were investigated by using scanning electron microscope (SEM) as well as energy dispersive spectrometer (EDS). Microhardness of sintered composite was also examined using Vickers hardness. The results were discussed in terms of the effect of milling time on the properties of the prepared powders and sintered bodies. The results revealed that the grain size of milled powders was about 55nm with a noticeable presence of agglomerates. Uniform distribution of nano-sized alumina particles in the copper matrix could be achieved with increasing milling time. The density of the sintered composites was affected by milling time of the starting powders and firing temperature. It increased with increasing milling time and firing temperature. Microhardness of the sintered bodies was found to be progressively increased with increasing of milling time of starting powders.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.