Abstract
Abstract：SiC/Si-B-C-N and SiC/SiC ceramic matrix composites were prepared through a combination of chemical vapor infiltration (CVI) and polymer impregnation pyrolysis process(PIP). The microscopic morphology and solid phase structure of the SiC/Si-B-C-N and SiC/SiC composites were investigated by SEM and XRD respectively. Moreover,the flexural strength and fracture toughness were measured using three point bending and single-edge notched beam test. Results showed that the formation of crystalline phases transformation was restrained by introduce BN into matrix phase, which might improve the stability of ceramic matrix composites. Furthermore, the flexural strength and fracture toughness of ceramic matrix composites increased to a maximum of 367 MPa and 26.81 MPa·m1/2 with the 30% PBN weight ratios which might be mainly caused by crack arresting, crack deflecting, micro cracks and fiber pullout.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.