Abstract
The ZrB2/SiC/Zr2Al4C5 multi-phase ceramics were fabricated by spark plasma sintering (SPS) at 1800 °C for 3 min under 20 MPa in an vacuum. Oxidation behavior of multi-phase ceramics were investigated using thermo gravimetric analysis (TGA) from 20 °C to 1500 °C and muffle furnace in stagnant air at 1200 °C. Samples were analyzed after oxidation by X-ray diffraction (XRD), scanning electron microscopy (SEM) along with energy dispersive spectroscopy (EDS) to determine the reaction products and to observe the microstructure. The results showed that the aluminium borate and mullite crystallize on the surface in the samples oxidized. The effect of Zr2Al4C5 content on the oxidation resistance of the ZrB2 ceramics were discussed respectively, and oxidation mechanism was also analysised.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.