Abstract
Gd2Zr2O7/ZrO2 (GZC) composite fibers were prepared by electro-spinning method. The XRD, XPS and Raman results showed that there were three crystalline phases, tetragonal phase ZrO2, cubic phase ZrO2 and defect fluorite phase Gd2Zr2O7 in GZC composite fibers. GZC fibers remained an intact fiber texture up to 1400 °C according to SEM photographs. The thermal conductivity of GZC fibers was between 0.173 W/(m·K) at 400 °C and 0.309 W/(m·K) at 800 °C, which was lower than that of 7YSZ under the same experimental conditions. The fiber sheet with density about 3.5 g/cm3 has thermal shrinkage less than 3% at 1400 °C. Hence, GZC fibers could be used as refractories for heat protection.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.