Abstract
AbstractPoly(lactic acid) (PLA) film plasticized with poly(ethylene oxide) (PEO) at various weight percentages (1–5 wt%) was prepared to improve the elongation, thus overcoming the inherent brittleness of the material. After optimization of the amount of PEO (4 wt%) through mechanical analysis, poly(ethylene glycol) (PEG), a well‐established plasticizer of PLA, was added (0.5–1.5 wt%) without hampering the transparency and tensile strength much, and again its amount was optimized (1 wt%). Neat PLA and PLA with the other components were solvent‐cast in the form of films using chloroform as a solvent. Improvement in elongation at break and reduction in tensile strength suggested a plasticizing effect of both PEO and PEG on PLA. Thermal and infrared data revealed that the addition of PEO induced β crystals in PLA. Scanning electron micrographs indicated a porous surface morphology of the blends. PEO alone in PLA exhibited the best optical clarity with higher percentage crystallinity, while PEG incorporation in PLA/PEO resulted in superior barrier properties. Also, the stability of the blends under a wide range of pH means prospective implementation of the films in packaging of food and non‐food‐grade products. © 2018 Society of Chemical Industry
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.