Abstract
Well-defined poly(methacrylate)s with liquid crystal side chains, designated as PPHM, were synthesized by a living anionic polymerization method. Introducing a short-length alkyl chain at the end of the side chain, the solubility of the polymer was improved, resulting in higher molecular weight polymers. While the highest weight-average molecular weight (Mw) of PPHM was 68k, it exceeded 100k for a slight-polydisperse PPHM. Wide-angle X-ray diffraction (WAXD) revealed that PPHM formed a smectic A phase with 2.7 nm layer spacing and that the layer structure is present even in the glassy state at room temperature. Molecular aggregation states of PPHM in surface regions of films were characterized by sum-frequency generation, grazing-incidence WAXD, and contact angle measurements. The results show that the PPHM with a larger Mw formed a layer structure parallel to the film plane. Although low Mw PPHM also maintained a layer structure, the structure became more random within internal regions. The surface reorg...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.