Abstract
The microstructure, hardness, and precipitate free zones (PFZ) of V55Ti30Ni15 alloys during heat treatment have been investigated in this study. The microstructure resulting from different heat treatment conditions has a great influence on hardness. The microstructure resulting from different heat treatment conditions has a great influence on hardness. Fine NiTi particles precipitate from the supersaturated V-matrix solid solution at 750 °C, increase in quantity until 800 °C, and then dissolve back into the V-matrix at 850 °C. The resultant hardness decreases with temperature until 800 °C, and then increases from 800 to 850 °C. The microstructure containing small NiTi precipitates resulting from the treatment of 18 h at 800 °C has a good soft condition for workability. PFZ formed at the grain boundary of V-matrix during heat treatment was observed. Vacancies depletion in V-matrix maybe led to the formation of PFZ.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.