Abstract
Ti6Al4V powders were produced by Argon gas atomization, the powder fraction ＜ 250μm was hot isostatically pressed (HIP) at 920°C and 140MPa. The properties of pre-alloyed powders and the compact were investigated in this paper. Powder particles are almost perfectly spherical. The microstructure of powder surface is approximate hexagonal cellular structure, the inner structure exhibits cellular αphase and needle-like martensiteα′ phase, these are resulting from the rapid solidification. After HIP, Ti6Al4V alloy has a Widmanstaten microstructure consisting of continuous grain boundary α（GBα）phase and β transformation structure, the grain size of GBα phase is in the range of 5～15μm . The tensile test at room temperature shows that strength of samples is 880MPa, the fracture surface exhibits obvious brittle cleavage fracture features including cleavage facets with river pattern and a few elongate dimples of different sizes and big voids at localized area.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.