Abstract
This paper provides critical data regarding the post-fire residual strength of Glass Fibre Reinforced Polymer (GFRP) reinforced concrete slabs. The residual tensile and bond strength of three types of GFRP reinforcing bars and the post-fire residual strength of a GFRP reinforced concrete slab are examined. For residual tensile strength, GFRP bars with a nominal diameter of 16 mm are exposed to temperatures up to 450 °C and tested after 24 h at room temperature. After 24 h, the specimens are loaded to failure at room temperature. For residual bond strength, pullout specimens are heated under various sustained load values. Finally, a full-scale GFRP reinforced concrete slab is tested at room temperature to evaluate the post-fire residual capacity after exposure to three hours of a standard fire. The residual tensile test results show that the bars that were exposed to 400 °C recovered at least 45% of the original strength while the residual bond strength is approximately 40% for pullout specimens that had experienced 300 °C. The post-fire residual strength of the slab is 68% of its room temperature flexural design strength with the bond loss at the ends of the slab being the governing mode of failure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.