Abstract
New single-buffer layers of YBiO3 and SmBiO3 have been proposed for YBa2Cu3O7−y (YBCO) and SmBa2Cu3O7−y coated conductors. Highly c-axis oriented YBiO3 and SmBiO3 buffer layers have been deposited on single-crystal LaAlO3 and SrTiO3, respectively, by a low-cost chemical solution deposition method in a temperature range as low as 730 to 800 °C in air. Precursor solution of yttrium nitrate, samarium nitrate, and bismuth nitrate has been deposited using spin coating and heat treated in air in a single stage to yield textured YBiO3 and SmBiO3 buffers. A very dense, smooth, pinhole-free, and crack-free morphology has been observed for both buffers. Dense, homogeneous, and epitaxially grown YBCO film with thickness about 300 nm has been obtained on YBiO3 buffer with onset critical temperature 90 K and Jc (77 K, self-field) over 3 MA/cm2. These results offer an effective alternative to prepare desirable buffer layer(s) for YBCO-coated conductors.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.