Abstract
AbstractPolyimide (PI) and polystyrene (PS) blend electrospun fibers are prepared by electrospinning method. PI and PS are not completely compatible due to the difference of solubility and surface energy in electrospinning precursor, so PI/PS electrospun fibers have some phase separations along the electric field direction under the high‐voltage electrostatic force. PI with high carbon conversion served as carbon nanofibers, PS with low carbon conversion served as porogenic sacrificial agent, so PI/PS‐based activated carbon nanofibers derived from PI/PS electrospun fibers with well‐controlled opening tubular structure are obtained via thermally induced phase separation process. The morphology and electrochemical performance of activated carbon nanofibers are investigated by structural analysis and electrochemical measurements. The relationships among pores structure, electrolyte character and electrochemical performance of activated carbon fibers are extensively evaluated. Activated carbon nanofibers derived from PI/PS (mass ratio = 1:2) electrospun fibers with nano scale opening tube wall structure show a small charge transfer resistance and the short electric double layers forming time, but also suitable average pore diameter (3.74 nm), high BET specific surface area (952.5 m2 g−1) and average pore volume (0.532 cm3 g−1). Then, a comprehensive electrochemical performance can also be achieved in organic electrolyte: high energy density (31.80 Wh kg−1), good power density (3094.05 W kg−1) and low internal resistance (1.24 Ω). The findings reveal a guideline for the preparation of polymer‐based hierachical porous and opening tubular structure activated carbon nanofibers for electrochemical energy conversion and storage devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.