Abstract
Wood modification treatments by substitution or blocking of wood hydroxyl groups with hydrophobic molecules are some of the novel approaches that may improve dimensional stability, weathering and decay resistance of wood. In this study, the Scots pine (Pinus sylvestris L.) wood was modified by ring opening polymerization of e-caprolactone to investigate the artificial weathering and decay resistance. In total, 672 h of artificial weathering was applied on modified wood by exposure of UV-light and water cycles. Additionally, decay test was carried out by using Coniophora puteana and Trametes versicolor fungi on the samples after leaching procedure. After weathering, the color change and contact angle measurements, as well as macroscopic observations revealed that the modified wood had significantly better surface properties than reference wood. FT-IR and SEM analysis proved that there was still polycaprolactone on the weathered surface with some minor crack formations of wood structure. The polycaprolactone modification effectively protected wood against decay even after leaching. This study also demonstrates that the polycaprolactone modification can provide a significant improvement on dimensional stability, as well as water repellence of Scot pine wood.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.