Polarisation behaviour of steel bar samples in concrete in seawater. Part 2: A polarisation model for corrosion evaluation of steel in concrete

Abstract

In the companion paper [Z.T. Chang, B. Cherry, M. Marosszeky, Polarisation behaviour of steel bar samples in concrete in seawater, Part 1: Experimental measurement of polarisation curves of steel in concrete, Corrosion Science 50(2) (2008) 357–364], influences of the experimental procedure on measured polarisation curves of steel in concrete in seawater were investigated. It was found that an undistorted full polarisation curve of a steel sample in concrete can be obtained by the two-test procedure to conduct separate anodic and cathodic polarisation tests and combine the two partial curves into one curve. However, polarisation curves of steel samples in concrete in seawater were found not to fit with the theoretical curves based on the kinetics of charge transfer reactions. This was considered to be due in the main to the influence of a passive film on the steel surface in concrete. This paper proposes an empirical model for the polarisation behaviour of steel in concrete based on the assumption of two major electrochemical processes taking place at the interfaces of steel/passive-film/concrete: one is the active corrosion process and the other is the passive film growth or dissolution process. Typical curve-fit results are presented using the proposed model to simulate the polarisation behaviour and to evaluate the corrosion rate and Tafel parameters of three types of steel corrosion in seawater: steel bars in concrete, new steel bars and corroded steel bars.