Abstract
Films of α-Ga2O3 grown by Halide Vapor Phase Epitaxy (HVPE) were irradiated with protons at energies of 330, 400, and 460 keV with fluences 6 × 1015 cm−2 and with 7 MeV C4+ ions with a fluence of 1.3 × 1013 cm−2 and characterized by a suite of measurements, including Photoinduced Transient Current Spectroscopy (PICTS), Thermally Stimulated Current (TSC), Microcathodoluminescence (MCL), Capacitance–frequency (C–f), photocapacitance and Admittance Spectroscopy (AS), as well as by Positron Annihilation Spectroscopy (PAS). Proton irradiation creates a conducting layer near the peak of the ion distribution and vacancy defects distribution and introduces deep traps at Ec-0.25, 0.8, and 1.4 eV associated with Ga interstitials, gallium–oxygen divacancies VGa–VO, and oxygen vacancies VO. Similar defects were observed in C implanted samples. The PAS results can also be interpreted by assuming that the observed changes are due to the introduction of VGa and VGa–VO.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.