Abstract
Photoelectrochemical (PEC) etching of InxGa1−xN in the KOH solution under illumination of a Hg-arc lamp is studied. An indium oxide surface layer is formed during PEC etching, which slows down the etching rate. The PEC etch rate of InxGa1−xN is determined by dissolution of indium oxides into the solution. Increase of the solution temperature results in an increase of solubility of indium oxides and thus enhances the PEC etch rate. It is found that stirring the solution can accelerate indium oxides to dissolve into the solution and increase the etch rate. The thick indium oxide layer on the PEC-etched InxGa1−xN surface can be effectively removed by the treatment of using a hot 6N HCl solution. A post-treatment by using a 3.2 M KOH solution can provide a smooth sidewall on the PEC-etched surface for the potential application to laser cavity.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.