Abstract
Phase transition and thermal depolarization of PbTiO3 piezoelectric ceramics with Double Perovskite modified were investigated. With 5mol% Double Perovskite (BFM, BNM, YNM, SNM), the PbTiO3 has a possibility to change the crystal structure to a large extent, and the sintering temperature can be controlled below 960°C. With increasing ionic radius difference between addition and PbTiO3, the crystal structure of modified PbTiO3, measured by synchrotron radiation changed from Tetragonal (P4mm) to Orthorhombic (Pmm2) and became more ordered (from 2×2×1 super cell to 6×2×2 super cell). The ordered Orthorhombic structure PT has higher phase transition temperature (496–540°C) than the Tetragonal PT (481°C). All modified PbTiO3 ceramics show high depolarization temperature. The depolarization temperatures of PT-BFM, PT-BNM, PT-YNM, and PT-SNM are 470°C, 480°C, 495°C, and 505°C, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.