Abstract
We report on the phase transformation behavior of Pb 0.91La 0.09Zr 0.65Ti 0.35O 3 (9/65/35) PLZT films grown on r-sapphire substrates via rf-magnetron sputtering. A complex microstructure results in these films depending on deposition and annealing conditions. A random equiaxed polycrystalline grain morphology was observed after rapid thermal annealing or furnace annealing when the as-deposited films were predominantly pyrochlore. Precipitate formation (100–150 nm) was observed in PLZT films that were deposited at temperatures in excess of 490°C with a perovskite structure, after furnace annealing at 700°C. We believe that this is related to internal stresses in the films due to both the lattice mismatch and the thermal expansion mismatch between the PLZT film and the sapphire substrate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.