Abstract
(1−x)Na0·5Bi0·5TiO3−xCaTiO3 ceramics with x = 0–0·2 were prepared by solid state sintering method. Structural and morphology studies carried out by X-ray diffraction and scanning electron microscopy indicate the change in crystal structure from rhombohedral to orthorhombic symmetry (R3C to Pnma). The morphotropic phase boundary of this system was found to lie around x = 0·08–0·14, where the orthorhombic and rhombohedral symmetries coexist. The orthorhombic phase is stabilised for x>0·14, indicating that the rhombohedral phase of Na0·5Bi0·5TiO3 is susceptible to orthorhombic distortion brought about by Ca substitution. Calcium substitution in Na0·5Bi0·5TiO3 caused an obvious decrease in peak temperature and a decrease in relative permittivity. The compositional variation of the fundamental dielectric behaviour is discussed in relation to the crystal chemistry of the system. The highest piezoelectric constant d33 of 85 pC N−1 is achieved for x = 0·1, with the coercive field of 18 kV cm−1 and the dielectric maximum temperature of 148°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.