Abstract

The phase relations in the CeO 2–Gd 2O 3–ZrO 2 system have been established after slowly cooling the samples from 1400 °C. Ceria has been used as a surrogate material in place of plutonia. About 80 compositions in Zr 1− x Gd x O 2− x /2, Ce 1− x Gd x O 2− x /2, Ce 1− x Zr x O 2.00, (Zr 0.5Ce 0.5) 1− x Gd x O 2− x /2, (Ce 0.5Gd 0.5) 1− x Zr x O 1.75+ x /4, (Zr 0.5Gd 0.5) 1− x Ce x O 1.75+ x /4, and (Ce 0.8Zr 0.2) x Gd 1− x O 1.5+ x / 2 were prepared by a three steps heating protocol. Based on the refinement of the XRD data, several phase regions namely; cubic fluorite type solid solution, C-type solid solution, and various biphasic regions could be delineated. This system showed the existence of a very wide cubic phase field. About 17.5 mol% GdO 1.5 was found to fully stabilize the cubic zirconia. On the other hand ceria did not stabilize the cubic zirconia. The anion-excess gadolinia, i.e., Gd 1− x Ce x O 1.5+ x was found to retain the C-type lattite unlike pure gadolinia. The ternary phase relations were mainly characterized by the presence of wide homogeneity ranges of fluorite type or C-type phases.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.