Abstract
AbstractThe objective of this study is to evaluate the high temperature behavior of γ TiAl-based alloy sheets containing AI2O3 particles, produced by a combination of vacuum induction melting, use of a CaO crucible, and direct sheet casting, over a wide temperature range. Alumina particles, having a tendency to coagulate during solidification of a TiAl ingot, are finely dispersed due to the disturbance of high frequency induction, and frozen without having enough time to grow in size by direct sheet casting. The TiAl sheet thus produced shows remarkable high temperature tensile strength which exceeds that of conventional ingots having the same composition and various different structures. This is determined to be attributable to the dispersion strengthening of finely dispersed AI2O3 particles whose diameter is from 100 to 500nm. Moreover, because of the small size of these alumina particles, the TiAl sheet does not show any significant retardation in high temperature ductility, which is often the case in conventional ceramic-reinforced intermetallic compound composites.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.