Oxidation resistant coatings in combination with thermal barrier coatings on γ-TiAl alloys for high temperature applications

Abstract

Titanium aluminide alloys based on γ-TiAl are considered of growing interest for high temperature applications due to their attractive properties. To extend the service temperatures above 750 °C, the oxidation behaviour has to be improved predominantly by protective layers. In the present study environmental and thermal protection coatings on gamma titanium aluminides were investigated. Nitride and metallic overlay coatings based on Ti–Al–Cr–Y–N and Ti–Al–Cr, respectively, were produced by magnetron sputtering techniques. Thermal barrier coatings (TBCs) of partially yttria stabilized zirconia were deposited onto Ti–45Al–8Nb, either pre-oxidized or coated with protective layers, applying electron beam physical vapour deposition (EB-PVD). Cyclic oxidation tests were performed at 900 °C and 950 °C in air. The nitride coating exhibited poor oxidation resistance when exposed at 900 °C providing no protection for γ-TiAl. The oxidation behaviour of the Ti–Al–Cr coating was reasonable at both exposure temperatures. During prolonged exposure the coating was depleted in chromium, resulting in the breakdown of the protective alumina scale. EB-PVD zirconia coatings deposited on γ-TiAl exhibited promising lifetime, particularly when specimens were coated with Ti–Al–Cr. The adherence of the TBC on the thermally grown oxide scales was excellent; failure observed was associated with spallation of the oxide scale. At 950 °C, TBCs on specimens coated with Ti–Al–Cr spalled after less than 200 thermal cycles caused by severe oxidation of γ-TiAl and reactions between the zirconia coatings and the thermally grown oxides.