Abstract
The oxidation behavior of SiC/BN/SiC ceramic matrix composites (CMCs) was evaluated from 400° to 800 °C in 100% O2 and 50% H2O/50% O2 gas mixtures. Thermogravimetric analysis (TGA) was utilized to measure weight change during controlled environment exposures at elevated temperatures for 1 and 50 hours. Oxidized CMCs and their oxides were studied post-exposure with scanning electron microscopy and energy dispersive spectroscopy. The oxidation onset and composition transition temperatures were evaluated. Key observations include oxide composition, oxide wetting, oxygen solubility in Hi-Nicalon SiC fibers and BN fiber coating oxidation and volatility behavior as a function of temperature. Degradation in wet environments at 600 °C was most extensive due to the formation of a non-wetting, non-protective surface oxide, allowing oxidant access to the BN fiber coatings followed by oxidation and volatilization. Implications of the CMC oxidation behavior are discussed for CMCs in service.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.