Abstract
An aluminized Ti-6Al-4V alloy was prepared successfully by hot-dipping aluminum under a protective argon atmosphere at 800°C. After isothermal oxidation tests at 800°C for various times, the weight gain of the hot-dipped aluminum coating showed the aluminized coating can provide a significant degree of protection against oxidation at 800°C. In addition, the coatings of as-coated hot-dipped aluminum and those after being exposed from 1 to 96h were also evaluated by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectrometer (EDS) analyses as well as Vickers microhardness test. Consequently, the microstructures of the hot-dipped aluminum coating were found to consist of an outer layer and a multilayer reaction zone. We found that a mixture of (Ti,V)Al3 and (Ti,V)Al2 phases exist in the outer layer and that (Ti,V)Al2, (Ti,V)Al, and (Ti,V)3Al phases form in sequence within the reaction zone after oxidizing for up to 96h.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.