Abstract
AbstractThe oxidation behavior and mechanism of aluminum oxynitride (AlON) powder exposed to air at elevated temperatures between 800°C and 1300°C was investigated by X‐ray diffractometry (XRD), scanning electron microscope (SEM), electron spin resonance (ESR), nuclear magnetic resonance (NMR), and simultaneous thermogravimetry, differential thermal analysis, and mass spectrometry techniques (TG‐DTA‐MS). The weight of AlON gradually increases to a maximum value at 1150°C and then decreases with further heating. Meanwhile, AlON powder undergoes chemical changes, as evidenced by lattice expansion, and turns eventually into alumina. ESR spectra reveal the occurrence of lone pair electrons in the oxidized products and the intensity of corresponding resonance signal increases before disappearing with the increase in temperature. Combined with the results of NMR and TG‐DTA‐MS, the measured data suggest that Al‐N in [AlO3N] tetrahedron and [AlO5N] octahedron are gradually oxidized into Al‐O‐N group with lone pair electrons, which causes continuous weight gain and lattice expansion. Further oxidation at higher temperatures results in alumina and N2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.