Abstract
AbstractOrange‐red‐emitting Eu3+‐doped Ca9Gd(PO4)7 phosphors have been obtained by a sol‐gel technique. These phosphors, excited by UV (270 nm) and near UV light (394 nm), emit orange‐red light in the range of 580–710 nm. The Ca9Gd(PO4)7:7 mol% Eu3+ phosphor annealed at 1100 °C shows the highest PL intensity. Judd‐Ofelt analysis reveals that the neighbor surroundings of Eu3+ ions are asymmetric, and the lowest asymmetry value is found at the dopant ratio of 7 mol%. The optimal phosphor excited by the wavelength of 394 nm displays an excellent thermal stability (∼76.4 % at 160 °C) with an activation energy of 0.163 eV. The corresponding CIE chromaticity coordinates (x; y) and color purity are calculated to be (0.5849; 0.3635) and 84.6 %, respectively. The quantum efficiency values of the Ca9Gd(PO4)7:Eu3+ phosphors coated on UV and near‐UV chips are 87.4 % and 5.1 %, respectively. It is the first time that the QE values of Ca9Gd(PO4)7:Eu3+‐based red and blue‐emitting LEDs are reported.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.