Abstract
The effects of both single- and two-step direct current (DC) annealing procedures on the magnetic properties (including the giant magneto-impedance (GMI)) of glass-coated Co66Fe6Si13B15 amorphous wires were evaluated. For both methods, the GMI ratio initially increased with the current intensity and reached a peak value before declining at higher current intensities. A maximum improvement of the GMI ratio of about five times was obtained for the two-step DC-annealed sample, while that for single-step DC-annealed samples was only 2.44 times. A higher GMI sensitivity was also observed for the two-step DC-annealed wires. The better GMI performance of the two-step DC annealed samples was attributed to the more homogeneously distributed precipitation in the matrix and the ordered circumferential magnetic domains on the surface. The results obtained further imply that DC annealing at a higher current intensity but over a shorter treatment time is a more efficient and energy-saving method for enhancing the GMI performance of Co-based amorphous wires for potential industrial applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.