Abstract
The effect of heat treatment on vacuum die-casting (VDC) AT72 magnesium alloy was studied. The optimal process of heat treatment was obtained. The result shows that the alloy was composed of α-Mg, Mg17Al12 and Mg2Sn. After solution treatment at 686K for 24h, Mg17Al12 completely dissolved in α-Mg matrix. With the aging treatment following solution treatment, Mg17Al12 kept precipitating in the matrix and along grain boundary. Moreover, Mg2Sn distributed along the grain boundary did not disappear after solution treatment at 686K. This indicates that Mg2Sn phase exhibits very high thermal stability. The heat treatment process was optimized with solution at 686K for 24h plus ageing at 473K for 18h, in the condition of which AT72 magnesium alloy exhibits a maximum hardness with value of 90.8Hv. The successful application of heat treatment for AT72 magnesium alloy could be attributed to the elimination of the air bubble in the casing through VDC. However, the porosity in the cast couldnt be efficiently eliminated by VDC, which result in the growth of shrinkage pore.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.