Abstract
TiO2 nanoparticles have been coated on the polypropylene (PP) copolymers using a milling method with temperature controller modification. These experiments were carried out at different milling temperature: 100 °C, 110 °C, 120 °C and 130 °C for 90 minute milling time for each experiment. Photocatalytic degradation of methylene blue (MB) was investigated using TiO2 coated PP copolymer which floats on the MB solution and illuminated under sunlight for 36 hours. It was found that TiO2 coated PP polymer at temperature of 100 °C resulted in optimum decomposition of MB solution. The concentration of MB in a test solution after 18 hours of exposure to the sun was 15.42%. The reaction rate constants (k) and the half‐reaction (t1/2) in the MB photodegradation using the catalysts with a coating temperature of 100 °C, are 0.106 hours−1 and 6.53 hours, respectively. This coated material is very potential for repeated use to purify bulk water in high sunlight intensity region.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.