Abstract
With the ongoing progress of mobile communication and new energy technologies, the market interest in high-frequency and high-power semiconductor devices has risen. Gallium nitride (GaN), a wide bandgap semiconductor material, has become a popular area of research in relevant fields. A sufficiently flat material surface can significantly enhance the device’s performance. Therefore, this paper explores the effect of oxidants on the quality of GaN surface during chemical mechanical polishing (CMP). Atomic force microscopy (AFM) was employed to examine the surface morphology of GaN after each CMP experiment. The aim was to evaluate the effect of specific slurry components on GaN surface quality. The results revealed that the introduction of oxidizers, particularly the potent oxidizer potassium persulfate (K2S2O8), was advantageous in reducing the surface roughness Sq and thus, enhancing the surface quality of GaN. The surface roughness (Sq) of GaN was reduced from 7.7 nm to 0.78 nm after the CMP process with the optimal components. AFM tests were conducted on different areas of the GaN surface within a range of 1 μm2, which revealed that clear images of the GaN atomic steps can be obtained, and the Sq can reach as low as 0.26 nm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.